opper-Based Cu-Zn Alloy Brass H65 C26800 AS9394 Tape Strip Coil Roll Bright Surface
|
|
商品の詳細:
お支払配送条件:
|
詳細製品概要
| タイプ: | ロッド | サイズ: | 30*30*1000mm |
|---|---|---|---|
| HV （柔らかさ）: | <130> | 老化するプロセス: | 利用可能 |
| 密度: | 8.25 | 老化する温度: | 260~426 |
| 熱拡張係数（μm /m.k）: | 16.7 | Liquidusの温度（℃）: | 980 |
| なれ: | 1.8~2.1 |
opper-Based Cu-Zn Alloy Brass H65 C26800 AS9394 Tape Strip Coil Roll Bright Surface
Yellow Brass, as it is commonly known, is among the highest zinc-containing brasses available to designers. Exhibiting a handsome yellow color associated with brasses this alloy finds use in many of the same applications as other high brasses. C2680 offers similar mechanical and physical properties to that of other brasses and is often found in applications requiring an economical copper-based alloy. Designers considering applications requiring a material capable of heavy deep drawing should consider alloy C2600.
Standard: JIS C2680, USN C26800
| Chemical Composition (%) | |||
| Cu | 64.0-68.0 | Zn | balance |
| Physical Properties | |||
| Density g/cm3 | 8.5 | Coefficient of thermal expansion 10-6 /℃ 20/℃-100/℃ | 20.3 |
| Electrical conductivity IACS%(20℃) | 27min | Thermal Conductility W/(m*k) | 121 |
| Modulus of elasticity (KN/mm2) | 103 | ||
Mechanical Properties:
| Temper | Tensile strength (RM, Mpa) | Yield Strength (Rp0.2, Mpa) |
Elongation A50 (%) |
Vickers Hardness (HV) |
| O | 295 min | - | 45 min | 90 max |
| 1/4 H | 330-415 | - | 40 min | 90-105 |
| 1/2 H | 370-440 | - | 30 min | 105-130 |
| 3/4H | 410-470 | - | 20 min | 130-145 |
| H | 430-510 | - | 14 min | 145-160 |
| EH | 510-610 | - | 8 min | 160-175 |
| SH | 565-630 | - | 5 min | 175-190 |
| ESH | 610-725 | - | - | 190-210 |