Waspaloy UNS N07001 W.Nr.2.4654 Ni-Cr-Co Based Superalloy Wire Rod
|
商品の詳細:
お支払配送条件:
|
詳細製品概要
| 化学組成: | ニッケルクロムコバルト | 応用: | N07001 |
|---|---|---|---|
| 形: | ロッド | 寸法: | 1.0mm |
| 色: | 銀白色 | 標準: | ASTM、ASTM ASME YB HB BJB GB |
Waspaloy is Ni-Cr-Co based superalloy.Excellent mechanical properties below 980 ° C (1800 ° F), high strength and oxidation resistance at 760-870 ° C (1400-1600 ° F).
Its strength is superior to that of alloy 718 at temperature above 1200-1300℉(650-750℃), and is generally comparable to Haynes R-41 alloy.
Waspaloy Material Composition
| C | Cr | Mo | Ni | Co | Al | Ti | Fe | Si | Mn | P | S | B | Zr | Cu |
| 0.03-0.1 | 18-21 | 3.5-5 | Balance | 12-15 | 1.2-1.6 | 2.75-3.25 | ≤2 | ≤0.15 | ≤0.1 | ≤0.015 | ≤0.015 | 0.003-0.01 | 0.02-0.08 | ≤0.1 |
Waspaloy Material Mechanical Properties
| Grade | Density | Melting Point | Mechanical Property | |||||
| Temperature | Tensile Strength | Yield Strength | Elogation min | Ψ min | Hardness min | |||
| Waspaloy | 8.22 |
1330-1360℃ 2426-2480℉ |
815℃ 1499℉ |
608 Mpa | / | 20 | 32 | 299-387 HBS |
Applications of Waspaloy
Gas Turbine Blades
Sealing Ring
Shaft
Turbine Disc
High Temperature Fasteners
Exotic Fasteners
Special Fasteners
| Alloy Name | Trade Name | UNS NO. | Germany Spec | French Spec | Specification |
| Waspaloy | / | N07001 | W.Nr.2.4654 | NC20K14 |
Waspaloy AMS5708 Waspaloy AMS5709 |
Waspaloy coefficient of thermal expansion
| θ/℃ | 20-100 | 20-200 | 20-300 | 20-400 | 20-500 | 20-600 | 20-700 | 20-800 | 20-900 |
| α | 12.47 | 12.73 | 13.04 | 13.53 | 13.97 | 14.47 | 15.05 | 15.68 | 15.95 |
Waspaloy thermal conductivity
| θ/℃ | 360 | 460 | 545 | 640 | 770 | 855 | 985 |
| W/(m·℃) | 16.8 | 18.3 | 20.2 | 22.4 | 24.1 | 25.3 | 28.0 |
Oxidation resistance in air with a duration of 100h
| θ/℃ | 900 | 1000 |
|
Oxidation rate g/(m2.h) |
0.083 | 0.226 |
Waspaloy welding
Can be fusion welded by argon-arc methods using a matched composition filler metal. If matching alloy is not available, then the nearest alloy richer in the essential chemistry (Ni, Co, Cr, Mo) shall be adopted.
Waspaloy machining
Heavy duty equipment and tooling shall be used to minimize work-hardening of it ahead of cutting.